0.12mm Alloy 5005 Temper H22 Thickness Aluminum Coil

0.12mm Alloy 5005 Temper H22 Thickness Aluminum Coil
0.12mm Alloy 5005 Temper H22 Thickness Aluminum Coil
0.12mm Alloy 5005 Temper H22 Thickness Aluminum Coil
0.12mm Alloy 5005 Temper H22 Thickness Aluminum Coil
0.12mm Alloy 5005 Temper H22 Thickness Aluminum Coil
Product Name
0.12mm Alloy 5005 Temper H22 Thickness Aluminum Coil
Brand
XINO STEEL
Price
USD/TON 2000
Material
1050, 1060, 1070, 1100, 1200, 2024, 3003, 3104, 3105, 3005, 5052, 5754, 5083, 5251, 6061, 6063, 6082, 7075, 8011, 8079, 8021
Steel Grade
O - H112, T3 - T8, T351 - T851 etc
Thickness
0.014mm-20mm
Width
60mm-2650mm
Lead Time
15-25 DAYS
Payment Term
TT OR LC
0.12mm Alloy 5005 Temper H22 Thickness Aluminum Coil belong to Al-Mg aluminum alloy, where magnesium is the main element inside. This kind of alloy is the most extensively used anti-rust aluminum and it has high strength, extraordinary fatigue resistance, excellent plasticity and corrosion resistance; it is non-heat treatable: it has high plasticity at annealed condition, good plasticity when semi-cold hardening, while low plasticity during cold hardening.

0.12mm Alloy 5005 Temper H22 Thickness Aluminum Coil



5005 alloy aluminum coil belongs to 5000 series alloy aluminum coil. 5005 aluminum coil of HuaWei Alu is certificated to ASTM, EN as well as JIS, etc. and it can be cut to size at customers’ need. Mg is the principal element in the 5005 aluminum coil and when it used as main alloying element or combined with Mn, high strength and no-heat treatable properties can be realized. 5005 aluminumcoil ofHuaWei Alu. has many tempers available, such as 5005-H12, 5005-H14, 5005-H16, 5005-H18,5005-H22, 5005-H24, 5005-H32, 5005-H34, 5005-H36, 5005-H38, etc.

6061 aluminum plate 6061 aluminum coil price.jpg

5005 aluminium coil can be cut to size at customers’ need. Mg is the principal element in the 5005 aluminium coil and when it used as main alloying element or combined with Mn, high strength and no-heat treatable properties can be realized. 5005 aluminium coil of Mingtai Al. has many tempers available, such as 5005-H12, 5005-H14, 5005-H16, 5005-H18,5005-H22, 5005-H24, 5005-H32, 5005-H34, 5005-H36, 5005-H38, etc.

Aluminium alloy 5005 contains nominally 0.8% magnesium. It has medium strength, good weldability, and good corrosion resistance in marine atmospheres. It also has the low density and excellent thermal conductivity common to all aluminium alloys. It is the most commonly used grade of aluminium in coil and coil form.

Aluminium alloy 5005 is a lean aluminium magnesium alloy which can be hardened by cold work: it is not heat treatable to higher strength.


0.12mm Alloy 5005 Temper H22 Thickness Aluminum Coil


  • Equivalent name: a5005, 5005a, al5005, aa5005, 5005 aa, aa 5005 grade etc

  • Temper


    • Soft HO, H11, H12, H13, H14, H15, H16, H17, H18, H19, H20, H21, H22, H23, H24, H25, H26, H27, H28, H29, H30, H31, H32, H33, H34, H35, H36, H37, H38, H39, H46, H111, H112, H114, H116, H131, H321 etc

    • T0, T2, T3, T4, T5, T6, T7, T8, T24, T32, T35, T73, T74, T83, T351, T354, T650, T651, T851 etc

  • Width: 610mm, 2650mm ( extra width ) etc

  • Thickness: 0.4mm, 0.6mm, 0.8mm etc


General Features

5005 is a non-heat treatable alloy with magnesium content. It can be strengthened (hardened) by cold working. It scores well in weld-ability, formability, and corrosion resistance (especially when anodized).

Forming

5005 has excellent formability, especially in softer tempers.

Welding

5005 alloy is noted for excellent welding characteristics. When 5005 material will be welded and then anodized

Machining

5005 machinability is generally fairly poor . Soft 5005 tempers machine worse than harder tempers. 5005 H34 and 5005 H38 can be machined, but with much more difficulty than many other aluminium alloys.

1070 aluminum coil supplier.jpg

Alloy 5005 Temper H22  Aluminum Coil Checmical Composition

  • Si ( Silicon ): ≤ 0.3

  • Cu ( Copper ): ≤ 0.2

  • Mg ( Magnesium ): 0.5 – 1.1

  • Zn ( Zinc ): ≤ 0.25

  • Mn ( Manganese ): ≤ 0.2

  • Cr ( Chromium ): ≤ 0.1

  • Fe ( Iron ): ≤ 0.7

  • Ti ( Titanium ): /

  • Others total: ≤ 0.15

  • Al ( Aluminum ): remainder


Mechanical Properties Of 5005 Alloy Aluminium Coils


Alloy
Temper
Specified thicknessTensile
strength
Yield
strength
Elongation
(MPa)(MPa)(%)
5005-H34 or 5005-H240.2~0.63mm138.179Min104min 3
0.63~1.2mmmin 4
1.2~6.3mmmin 5
6.3~50mmmin 8
5005-H32 or 5005-H220.2~600mm118-158Min83min 3

5005-H14145-186min118min1


5005 Properties By Temper (Typical)


AlloyFormTemperTensile StrengthYield StrengthElongation
5005coilH12201910
5005coilH1423226
5005coilH1626255
5005coilH1829284
5005coilH32201711
5005coilH3423208
5005coilH3626246
5005coilH3829275

Application Of 5005 Alloy Aluminium Sheet Roll


5005l aluminum coil strength and 3003 equivalent, weld metal, good workability 5005 aluminum plate and 3003 alloy similar, with moderate strength and good corrosion resistance. Anodic oxide film is more bright than the oxide film on the 3003 alloy, and is consistent with the tone of the 6063 alloy.

5005 aluminum coil is also a non-heat treatable alloy and it can be strengthened (hardened) by cold working. However, hot working should not normally be necessary. Besides, it scores well in formability, especially in softer tempers. The machinability of 5005 aluminum coil is generally fairly poor. 5005-H34 and 5003-H38 can be machined, but with much more difficult than many other aluminum alloys.

The main content of 5005 aluminium coil is Fe, Mg and Si, thus, it has good weld-ability and resistance to correction (especially when anodized), which resulting in suitable for marine applications. 5005 aluminium coil is also a non-heat treatable alloy and it can be strengthened (hardened) by cold working. However, hot working should not normally be necessary. Besides, it scores well in formability, especially in softer tempers. The machinability of 5005 aluminium coil is generally fairly poor. 5005-H34 and 5003-H38 can be machined, but with much more difficult than many other aluminium alloys.

Alloy 5005 Aluminium coil is typically used for:

  • Buildings – Roofing, Cladding, Corrugated coil

  • Signage, Road Signs & Name Plates

  • Food & Chemical Equipment

  • Furniture

  • Anodised Parts

  • HVAC Equipment

  • Packaging

  • Pipe and Tube

  • Can Bodies

Commonly used in the manufacture of appliances, small boats, gas lines, refrigerator panels, and utensils. 5005 is also used in architectural components, and as an electrical conductor. Especially useful where excessive finishing costs are encountered in the use of 3003 alloys due to surface roughness upon drawing.


1050-aluminum-coil.jpg


Alloy 5005 Temper H22  Aluminum Coil Packing

Standard export package.

Aluminium coil of packaging meet the export standard. Plastic film and brown paper can be covered at customers’ need. wooden case or wooden pallet is adopted to protect products from damage during the delivery.

Standrad export seaworthy wooden pallet with

  1. Plastic film ( HDPE, PVC, PE or PET etc ) protection.

  2. Hard Kraft Paper.

  3. Steel Bar Bunch.

  4. Wooden plate.


Send a Message

If you want to ask anything just fill in the form below and send us.

Name: Preston        time:2022-04-29 15:47:54
I customized this aluminum coil for my customer. It works perfectly by miracl... It looks awesome, and I’ve received many compliments.

Name: Naylor        time:2022-04-07 11:06:30
I have purchased these aluminum coil several times and they are wonderful quality as always!!

Write a review

Featured Products